Introduction
Titanium plates are manufactured according to both national and international standards.
-
National Standards: GB/T 3621-2007, GB/T 13810-2007
-
American Standards: ASTM B265, ASTM F136, ASTM F67, AMS 4928, and AMS 4911
AMS 4911 Titanium 6Al-4V (also known as Grade 5 Titanium) is the most widely used titanium alloy. It offers an excellent combination of high strength, low weight, and superior corrosion resistance, making it suitable for aerospace, medical, marine, and automotive industries.
Specification
| Product Form |
Size Range / Thickness |
| Titanium Coil |
0.012" – 0.125" |
| AMS 4911 6Al-4V Titanium Sheet |
0.012" – 0.125" |
| AMS 4911 6Al-4V Titanium Plate |
0.125" – 4" |
| Common Sheet/Plate Sizes |
0.032" × 36" × 96"0.040" × 36" × 96"0.063" × 36" × 96"0.071" × 36" × 96"0.080" × 36" × 96"0.090" × 36" × 96" |
| Maximum Dimensions |
Width ≤ 59", Length ≤ 118" |
Mechanical Properties
| Property |
Value |
| Tensile Strength (Min) |
900 MPa |
| Yield Strength at 0.2% Offset (Min) |
825 MPa |
| Elongation (A50mm, Min) |
10% |
| Hardness (Max) |
36 HRC |
Chemical Composition
| Element |
Min (%) |
Max (%) |
| Aluminum (Al) |
5.50 |
6.75 |
| Vanadium (V) |
3.50 |
4.50 |
| Iron (Fe) |
— |
0.30 |
| Oxygen (O) |
— |
0.20 |
| Carbon (C) |
— |
0.08 |
| Nitrogen (N) |
— |
0.05 (500 ppm) |
| Hydrogen (H) |
— |
0.015 (150 ppm) |
| Yttrium (Y) |
— |
0.005 (50 ppm) |
| Other Elements, Each |
— |
0.10 |
| Other Elements, Total |
— |
0.40 |
| Titanium (Ti) |
Remainder |
— |
Applications
1. Aerospace Industry
Titanium 6Al-4V plates are widely used in aircraft engines, structural parts, and airframe components due to their lightweight, high strength, and resistance to high-temperature oxidation and corrosion, effectively enhancing performance and extending service life.
2. Medical and Healthcare
With excellent biocompatibility, titanium plates are ideal for medical implants such as artificial joints, dental implants, bone plates, and prosthetics. They provide durability, lightness, and compatibility with human tissue.
3. Marine Engineering
Titanium 6Al-4V exhibits outstanding resistance to seawater corrosion, making it suitable for offshore oil and gas applications, subsea pipelines, and marine structures, where long-term durability is essential.
4. Automotive Manufacturing
As performance demands rise, titanium alloys are increasingly used in automotive components such as engine hoods, connecting rods, and exhaust systems. Their strength, toughness, and lightweight properties enhance safety and fuel efficiency.
Summary
AMS 4911 Titanium 6Al-4V Sheet and Plate combine strength, light weight, corrosion resistance, and biocompatibility. They are key materials for aerospace, medical, marine, and automotive applications, and their use continues to expand with advances in technology and manufacturing.